Studi Pengelasan TIG pada Material SUS 304 Ditinjau dari Kekuatan dan Sifat Mekanis
TIG Welding Study on SUS 304 Material in Terms of Strength and Mechanical Properties
DOI:
https://doi.org/10.59525/gej.v1i3.159Keywords:
Mechanical Properties, Sensitization, SUS 304, Tensile Strength, TIG WeldingAbstract
TIG (Tungsten Inert Gas) welding is a metal joining method widely used in industry because it is capable of producing smooth, clean, and high-precision welds. However, in austenitic stainless steel SUS 304, the welding process often causes changes in mechanical properties due to thermal cycling that affect tensile strength, hardness, and toughness. This study aims to analyze the effect of TIG welding on the strength and mechanical properties of SUS 304 and to identify optimal parameters that can maintain the material's structural integrity. The method used is a qualitative approach with direct observation of the welding process, in-depth interviews with practitioners, and documentation of the results of tensile, hardness, and toughness tests in the laboratory, which were carried out for three months in the workshop and material laboratory. The results show that TIG joints in SUS 304 have tensile strength close to that of the parent material, the hardness distribution varies between zones, and the toughness decreases especially under high heat input conditions. The analysis of the results also confirms that welding parameter control plays an important role in preventing grain growth and sensitization phenomena that reduce mechanical properties. In conclusion, this study provides theoretical contributions to strengthen the study of the relationship between welding parameters and the mechanical properties of SUS 304, as well as practical contributions in the form of guidance for industry in optimizing joint quality.
References
Almanda, M. D., Yudo, H., & Budiarto, U. (2020). Analisa Pengaruh Variasi Sudut Kampuh Terhadap Kekuatan Tarik Aluminium 6061 Dengan Gas Pelindung Argon Grade A dan Grade C Pada Pengelasan GTAW. Jurnal Teknik Perkapalan, 9(1), 130-138.
Bashoruddin, M., & Nasution, A. H. (2022). Pengaruh Kuat Arus Pada Kekuatan Tarik Aluminium 6061 Dengan Pengelasan Tungsten Inert Gas (Tig). PISTON (Jurnal Ilmiah Teknik Mesin Fakultas Teknik UISU), 7(1), 20-28.
Djuanda, D., Nurlela, N., Adam, A., & SYAHRIL, M. (2021). Analisis Pengaruh Media Pendingin terhadap Struktur Mikro Sambungan Pengelasan Baja AISI 1045 pada Proses Las MIG. Jurnal Teknik Mesin Teknologi, 22(1), 43-54.
Ismawan, F., & Syahbuddin, S. (2022). Optimasi Parameter Pengelasan Gmaw Pada Baja Tahan Karat AISI 409 untuk Mengurangi Jumlah Spatter. Teknobiz: Jurnal Ilmiah Program Studi Magister Teknik Mesin, 12(3), 184-191.
Jordi, M., Yudo, H., & Jokosisworo, S. (2017). Analisa Pengaruh Proses Quenching Dengan Media Berbeda Terhadap Kekuatan Tarik dan Kekerasan Baja St 36 Dengan Pengelasan SMAW. Jurnal Teknik Perkapalan, 5(1).
Lasno, M., Purwanto, H., & Dzulfikar, M. (2019). Pengaruh Variasi Arus Pengelasan Tig (Tungsten Inert Gas) Terhadap Sifat Fisik Dan Mekanik Pada Stainless Steel Hollow 304. Majalah Ilmiah Momentum, 15(2).
Muliadi, D., Ridho, R., & Marpaung, C. P. (2018). Pengaruh Kuat Arus terhadap Sifat Mekanis dan Struktur Mikro Sambungan Las Smaw Baja Sa 516 Gr. 70. Mekanik, 4(2), 329177.
Niko, D. D., & Basuki, E. A. (2022). Pengaruh Penambahan Zirkonium pada Paduan Fe-17Ni-17Cr-7, 7Al-4Cu Terhadap Oksidasi Isotermal. Jurnal TEDC, 16(3), 220-230.
Prayitno, H., Bahrawi, A., Wirawan, W. A., Sakti, G., Pambudiyanto, N., & Wulansari, A. (2024). Pengembangan Keterampilan Las Listrik SMAW Pada Siswa Sekolah Menengah Kejuruan (SMK) Di Workshop Politeknik Penerbangan Surabaya. TEKIBA: Jurnal Teknologi dan Pengabdian Masyarakat, 4(2), 213-227.
Prayogi, A. (2019). Analisa pengaruh variasi media pendingin pada perlakuan panas terhadap kekerasan dan struktur mikro baja karbon rendah. Jurnal Polimesin, 17(2), 83-90.
Priyotomo, G., Gede, N., Astawa, I. N. G. P., & Rokhmanto, F. (2021). Efek Perlakuan Panas Terhadap Sifat Mekanik Logam Stainless Steel Seri J4. Journal Teknik, 42(2).
Rahmatika, A., Ibrahim, S., Hersaputri, M., & Aprilia, E. (2019). Studi pengaruh variasi kuat arus terhadap sifat mekanik hasil Pengelasan GTAW alumunium 1050 dengan filler ER 4043. Jurnal Polimesin, 17(1), 47-54.
Sai'in, A., & Muzaki, M. (2020). Pengaruh kecepatan putar, gaya gesek dan waktu gesek terhadap struktur mikro dan laju korosi hasil pengelasan proses las gesek material berbeda baja SUH 3 dan SUH 35. Jurnal Rekayasa Mesin, 15(1), 10-19.
Sinaga, R., Dahlan, D., & Maulana, E. (2020). Perancangan Pembangkit Listrik Tenaga Magnet Dengan Kapasitas 100 Watt. In Prosiding Seminar Rekayasa Teknologi (SemResTek) (pp. KE1-KE10).
Sukaryo, S. G., Badriyana, B., & Sebleku, P. (2018). Pengaruh penambahan Molibdenum terhadap morfologi struktur mikro, sifat mekanik dan ketahanan korosi paduan Zr-Nb untuk material implan. Metalurgi, 29(1), 17-26.
Wang, J., Shen, Y. F., Xue, W. Y., Jia, N., & Misra, R. D. K. (2021). The significant impact of introducing nanosize precipitates and decreased effective grain size on retention of high toughness of simulated heat affected zone (HAZ). Materials Science and Engineering: A, 803, 140484.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Global Education Journal
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.